One-component room temperature vulcanized silicone rubber

The curing reaction of one-component room temperature vulcanized silicone rubber is initiated by the moisture in the air. The commonly used cross-linking agent is methyltriacetoxysilane. Its Si-OC bond is easily hydrolyzed. Acetoxy groups are combined with hydrogen groups in water to form acetic acid. The hydroxyl groups in water are transferred to the original acetoxy groups. In position, it becomes trihydroxymethylsilane. Trihydroxymethylsilane is extremely unstable and easily condenses with linear silicones whose terminal groups are hydroxyl groups to form a cross-linked structure. In general, the silicone rubber containing silanol end groups and various compounding agents such as fillers, catalysts, and cross-linking agents are packed into sealed hoses. When used, they are squeezed out of the container and vulcanized by the moisture in the air Elastomer, release low molecular weight at the same time. In addition to the methyl triacetoxysilane, the cross-linking agent may be a silane containing an alkoxy group, an oxime group, an amine group, an amide group, or a ketone group. When crosslinked with alkoxy group, alcohol is released, which is called dealcoholized one-component room temperature vulcanized silicone rubber. When crosslinked with oxime group, oxime is formed, called deoxidized room temperature vulcanized silicone rubber. Different types of agents, one-component room temperature vulcanized silicone rubber can be deacidified, deoxidized, dealcoholized, deamined, deamidated, and deketoned.