Surface chemistry includes an H, -OH group, pH, moisture, ignition loss, and the like. The surface chemistry of silica has a great influence on the physical properties and vulcanization rate of the rubber. Practice has shown that white carbon black can adsorb with many small molecules of organic matter, and the surface hydroxyl groups can strongly hydrogenate with water molecules. This is the main reason why we often say the hydrophilicity of silica. Alcohols and amines can also produce strong hydrogen bonding with white carbon black. This effect is especially important for the application of silica in the rubber industry. In silica-reinforced rubber, the surface of silica It will strongly adsorb the accelerator, anti-aging agent and other related compounding agents in the rubber to cause the vulcanization delay phenomenon. In order to prevent the above phenomenon, some amines and alcohols may be added to preferentially adsorb on the surface of the white carbon black to prevent or Attenuate the adsorption of the promoter by the silica. Polyfunctional alcohols or amines are more adsorptive than monofunctional. Therefore, a polyfunctional compound such as ethanolamine, ethylene glycol or triethanolamine is often used as an activator in the silica rubber compound. The adsorption of white carbon black on the accelerator is much greater than the adsorption of carbon black on the accelerator. The smaller the particle size, the lower the pH value and the stronger the adsorption force. The adsorption energy of the promoter increases as the operating temperature increases.