Product introduction:
IOTA ST2 water-based nanometer high hardness self-cleaning
coating is light yellow transparent liquid, which is prepared by nanometer
coating technology. This product contains nanoscale materials, coating on the
surface of the substrate, has a strong ability to reduce surface tension. Under
the action of ultraviolet and visible light, hydroxyl radicals are generated,
which have strong catalytic degradation and self-cleaning functions. Effective
decomposition of various surface oils. It can effectively kill a variety of
bacteria, and can decompose and harm the toxins released by bacteria or fungi.
At the same time, it also has the functions of removing formaldehyde,
deodorizing, anti-fouling and purifying air.
Application:
Metal surface anti-oxidation, waterproof, anti-pollution
treatment, glass surface hate water, anti-pollution, anti-ultraviolet coating,
ceramic, stone surface waterproof, anti-pollution, anti-corrosion treatment,
solar cell anti-pollution, weather-resistant coating.
How to use?
This product is simple to operate, high fastness, no residue, 10 - 30 minutes after normal temperature spraying or dipping and pulling, then heated at 170 C for 5 minutes, or cured at room temperature for 1-3 days(Noted: 5% ~ 8% curing agent needs to be added for curing at room temperature)
Performance characteristics:
l Good hydrophobicity after complete curing, water contact angle of 100 degrees or more, water droplets rolling off water marks.
l Completely transparent and colorless after curing, with high light transmittance.
l Hardness up to 8H, contains nano titanium oxide, anti-aging, long-lasting self-cleaning.
l Easy to operation, water-based paint ,no residue.
l Activated under light condition, nano titanium oxide can have antibacterial and deodorant effect and decompose bacteria and mold.
l High temperature resistance, use at temperatures up to 200 °C, no change in coating.
A highly dense and stable nano-super-hydrophobic
transparent ceramic coating is formed on the surface of the treated object, the
hardness can reach 8H, and the dust and dirt attached to the surface can easily
slide down with the water, applied to the surface of photovoltaic glass,
battery board, glass curtain wall and other objects, it can have the special
functions of durable self-cleaning, dust-proof, additional investment,
dew-proof, anti-bacterial decomposition of organic substances, etc. Provide
more convenience for people's life, and improve the service life of the battery
panels.
Performance and indicators:
No.
Project
Index
Test
standard
1
Appearance
Light Yellow transparent liquid
Visual
inspection
2
Weight
Solid Component
35%
3
Coating
thickness(Wet film)
10-20μm
4
Coating
thickness(Dry film)
1-5μm
5
Hardness(Pencil hardness)
5-8H
GB/T 6739-1996
6
Adhesion
Level
0
GB/T 9286-1998
7
Colour(After curing)
Transparent
coating
8
Natural
hardening time
10min
dry, 1-3 days cure
Note:
5% ~ 8% curing agent needs to be added at room temperature
9
Heat
curing condition
10min
dry,170℃,5min
10
Shelf
life (month)
12
months
Packaging
and transportation:
l 25 kg plastic drum or 200 kg iron drum packaging.
l Install in clean and dry containers and store in a ventilated and dry warehouse.
l This product is transported as non-dangerous goods.
l Shelf life: 12 months
l Brand: IOTA